Test

N

Conditions

Standard

Time

High Humidity Storage Test

22

Ta = 85°C, RH = 85%

Within +-20% of the initial value.
Note; | Vos |<=(Upper standard limit +5mV)

1000hrs

High Temperature Bias Test

22

Ta=110°C Ic is the bias current

Same as above

1000hrs

Heat-Proof Test for Soldering

22

Dipped in the 260+-5°C
solder up to the 1mm part from the body.

Same as above

10+-1sec

High Temperature Storage Test

22

Ta=125°C

Same as above

1000hrs

Heat Cycles Test

22

-40°C	=>>	Room Temperature	=>>	+125°C
30min	<<=	5min	<<=	30min

Same as above

50 cycles

Test Item

N

Test Condition

Standard

Test Time

High Humidity Storage Test

22

Ta=85°C, RH = 85%

Within +-20% of the initial value.
Note; | Vos |<=(Upper standard limit +5mV)

1000hrs

High Temperature Bias Test

22

Ta=125°C
Ic is the bias current

Same as above

1000hrs

Heat-Proof Test for Soldering

22

Dipped in the 300+-5°C
solder up to the 1mm part from the body.

Same as above

5+-2 sec

High Temperature Storage Test

22

Ta=150°C

Same as above

1000hrs

Heat Cycles Test

22

-55°C	=>>	Room Temperature	=>>	+150°C
30min	<<=	5min	<<=	30min

Same as above

50 cycles